At ace they have steel nipples that are about 2 inch diameter by 1 foot. Its about 6 dollars for a piece like this. Im just curious about using it as a chamber.

Using the nipple would be much easier because the ends are already threaded and would require no welding. I could just screw on my piece and be ready to go.

They have no rating marked on the nipple or on the tag. It just says galvanized steel nipple. It also says SCH 40.

Would this be safe as a chamber at 200 psi? What about 300 or 400?

if a soda botle can hold 150...

ive used the 1 inch sel nipple at 300 before

The soda bottle thing makes perfect sense. It hadent crossed my mind though. Haha.

Im pretty sure it would be ok to use but i wanted to be sure. And i also wanted to know if anyone else has used one before.

On Ace's website I remember reading that the nipples are rated to 300 PSI (WOG), and 150 PSI for steam.

That is the same steel pipe that a lot of people make pneumatics and even hybrids out of, so you should be fine.

i would have no problem to put 700psi in a sch40 steel pipe

this makes me want to burst test steel pipe
but like spudfarm said i wouldnt hesitate to put 700 psi into the pipe
most steel nipples are welded lengthwise so chances are the metal in the the nipple will fail before the weld because most welding rod is made from a higher grade metal note:im not sure exactly how the friction stir welding process works but i assume that the welds are usually higher strength than the base metal

if you are really worried abot the nipple failing you can order pressure rated ones from mcmaster

Read through this.

http://www.spudfiles.com/forums/the-fai ... 15393.html

Make sure you save a copy of this too.

http://www.engineeringtoolbox.com/wroug ... _1123.html

marpat wrote: i assume that the welds are usually higher strength than the base metal

steel becomes brittle after welding, i welder to steel pieces tougether and put pressure on the joint and when it first have bent a tiny bit it is ruined, it will become styrofoam just made of steel.

now that i am done testing with my small hybrid made of those pipes i will send them to Larda for pressure testing

SpudFarm wrote:

marpat wrote: i assume that the welds are usually higher strength than the base metal

steel becomes brittle after welding, i welder to steel pieces tougether and put pressure on the joint and when it first have bent a tiny bit it is ruined, it will become styrofoam just made of steel.

now that i am done testing with my small hybrid made of those pipes i will send them to Larda for pressure testing

The steel only gets harder if you cool you piece too fast.