Does tarnish affect copper's strength?
Title pretty much says it all.
It is winter over here and some of my copper chamber and barrel have begun to oxidize, tarnish. So i was just wondering is it hinders the strength of my chamber. Also, what would be a good way to get rid of it? Polish or sanding i presume?
It is winter over here and some of my copper chamber and barrel have begun to oxidize, tarnish. So i was just wondering is it hinders the strength of my chamber. Also, what would be a good way to get rid of it? Polish or sanding i presume?
4SPC, My 4" piston 3" porting cannon
Memo:
Fix up copper cannon
Fix up 4SPC
Start Stirrup pump
Start Toolies piston bazooka
Memo:
Fix up copper cannon
Fix up 4SPC
Start Stirrup pump
Start Toolies piston bazooka
- dudeman508
- Specialist 2
- Posts: 237
- Joined: Thu Jul 03, 2008 9:19 pm
I would think that sanding it would decrease the burst preasure, but it wouldnt be enought to make a difference.
I just use steel wool, and the copper would have to be EXTREMELY rusted and left in the rain for a very long time to affect the actual pipe.
Usually the tarnish encounter is so thin a few strokes with fine steel wool will get it to a shine again.
Nothing to worry about
Usually the tarnish encounter is so thin a few strokes with fine steel wool will get it to a shine again.
Nothing to worry about
Add me on MSN to chat about whatever!
Thanks, just curious. I knew it really wouldnt hinder its performance, but its better to be sure than not. I wonder how much would need to be tarnished in order for its strength to be diminished.
Hm...
Hm...
4SPC, My 4" piston 3" porting cannon
Memo:
Fix up copper cannon
Fix up 4SPC
Start Stirrup pump
Start Toolies piston bazooka
Memo:
Fix up copper cannon
Fix up 4SPC
Start Stirrup pump
Start Toolies piston bazooka
- Davidvaini
- Sergeant 4
- Posts: 1315
- Joined: Tue May 29, 2007 8:58 pm
There are a couple good ways to get rid of the tarnish.
CLR is a very good cleaner that really works against calcium lime and rust. It cleans old coins really well.
There is also this powder stuff that when mixed with a little water becomes a paste. It is called CAMEO its copper, brass and porclean cleaner.
I have used the CAMEO stuff on the copper pipes for my bathroom and it got rid of all the green yucky crap instantly. It then started to polish the pipe quite nicely getting rid of everything else that was left.
CLR is a very good cleaner that really works against calcium lime and rust. It cleans old coins really well.
There is also this powder stuff that when mixed with a little water becomes a paste. It is called CAMEO its copper, brass and porclean cleaner.
I have used the CAMEO stuff on the copper pipes for my bathroom and it got rid of all the green yucky crap instantly. It then started to polish the pipe quite nicely getting rid of everything else that was left.
- daxspudder
- Specialist 3
- Posts: 300
- Joined: Thu Apr 24, 2008 10:22 pm
unlike iron, when copper oxidizes (creating verdigris vice rust) it degrades the metal almost immeasurably, even thick verdigris ("ver-d'i-gree") has almost no effect on the metal it "grows" on(as long as it is copper carbonate...from air, not copper chlorate... from sea water)... so other than making it look bad it shouldnt hurt... there are however exceptions... like if it appears to be coming out of solder points... insufficient cleaning before applying flux can cause premature erosion of welds and create minor cracks in which verdigris can increase and even be caused by a reaction with excessive flux left behind...
"<I>For dare to be peace, I have to keep at it everyday, da Man doesn't take days off so neither can I</I>" -<B>Bob Marley</B>, day before a performance, a day after being shot in the chest. "<I>If you are the big, big tree, we are the small axe, ready to cut you down!</I>" -Bob again :brave:
No. Copper tarnish is a layer only molecules thick, and it's a protective tarnish - that is, in forming, it protects the lower layers from tarnishing the same.LikimysCrotchus5 wrote:So i was just wondering is it hinders the strength of my chamber.
Where rust can go the whole way through the thickness of steel, copper tarnish is only on the very surface, not enough to affect it.
Personally, I'd just leave it - tarnish is not the prettiest thing in the world, but cleaning it is a lot of extra maintenance that doesn't need doing.
Does that thing kinda look like a big cat to you?
- mark.f
- Sergeant Major 4
- Posts: 3627
- Joined: Sat May 06, 2006 11:18 am
- Location: The Big Steezy
- Has thanked: 52 times
- Been thanked: 53 times
- Contact:
You guys are forgetting the fact that after you clean and polish it, it will just tarnish again in a matter of days, depending on the type of climate you live in (I live in Louisiana, so it's a matter of 2-3 days).
If you don't like it, clean it and then coat the chamber in some sort of protective varnish or clear-coat.
If you don't like it, clean it and then coat the chamber in some sort of protective varnish or clear-coat.
-
- Sergeant Major
- Posts: 3197
- Joined: Wed Mar 28, 2007 9:48 am
- Location: Greenwood, Indiana
- Has thanked: 5 times
- Been thanked: 15 times
- Contact:
Another excellent cleaner, and the fastest and simplest, is Muriatic Acid (Hydrochloric Acid), which is available at most hardware stores.
20% HCl (what's in the jug you buy) will remove copper tarnish almost instantly without any scrubbing. Solder for copper pipe contains acid, the HCl does the same thing the flux in the solder does, it dissolves copper oxides. The HCL will remove the oxide coat but it won't polish the metal like sanding will.
You must thoroughly rinse the acid off. The acid will eat holes in your fingers, clothes etc. so be careful with it. The used acid can be flushed down a sink with large amounts of water.
Like markfh11q said, the copper will re-oxidize unless it is coated with something like a suitable laquer or a thin coat of oil.
I wouldn't use steel wool. Steel wool tends to leave fragments of iron behind that will rust within hours. The prefered abrasive for cleaning copper is fine wet-dry sand paper. You can use it dry, or better yet, use water as the lubricant. Sand paper is how plumbers clean pipe before soldering, I've never heard of a plumber using steel wool.
20% HCl (what's in the jug you buy) will remove copper tarnish almost instantly without any scrubbing. Solder for copper pipe contains acid, the HCl does the same thing the flux in the solder does, it dissolves copper oxides. The HCL will remove the oxide coat but it won't polish the metal like sanding will.
You must thoroughly rinse the acid off. The acid will eat holes in your fingers, clothes etc. so be careful with it. The used acid can be flushed down a sink with large amounts of water.
Like markfh11q said, the copper will re-oxidize unless it is coated with something like a suitable laquer or a thin coat of oil.
I wouldn't use steel wool. Steel wool tends to leave fragments of iron behind that will rust within hours. The prefered abrasive for cleaning copper is fine wet-dry sand paper. You can use it dry, or better yet, use water as the lubricant. Sand paper is how plumbers clean pipe before soldering, I've never heard of a plumber using steel wool.
- john bunsenburner
- Sergeant 5
- Posts: 1446
- Joined: Sun Oct 19, 2008 5:13 am
It is important to wash the acid of well though as it will form copper chloride which will weaken the chamber. I suggest leavign it be...
"Did you ever stop to think that out of the seven deadly sins envy is the only one which doesn't give the sinner even momentary pleasure"-George Will
- daxspudder
- Specialist 3
- Posts: 300
- Joined: Thu Apr 24, 2008 10:22 pm
um HCL will produce copper chloride, the damaging verdigris(<<<means rust, but on copper not iron) rather than copper oxide, the tarnish... or course washing it off will not cause copper chloride, but the copper will tarnish as water help oxidize copper... use copper wool.... like steel wool but made from copper sheep instead
"<I>For dare to be peace, I have to keep at it everyday, da Man doesn't take days off so neither can I</I>" -<B>Bob Marley</B>, day before a performance, a day after being shot in the chest. "<I>If you are the big, big tree, we are the small axe, ready to cut you down!</I>" -Bob again :brave:
- Davidvaini
- Sergeant 4
- Posts: 1315
- Joined: Tue May 29, 2007 8:58 pm
if you use that cameo you dont even need sand paper or anything to polish it...
after you are done, just apply some sort of clear coat and you are good to go.
after you are done, just apply some sort of clear coat and you are good to go.
Hi guys, new user here. Just thought this was a good opportunity to provide some input.
The more you polish any metal, the more it wears away at the material, especially with softer metals. Not a problem if you will only use a launcher for a few years, but if you want to use it in say, 30 years from now, it may weaken the tubing a bit. you would be best off letting the copper develop a natural patina (the brown patina looks great on copper, imo)
some people go through all kinds of trickery to force copper to look weathered. The oxidization is what makes copper roofing and the Statue of Liberty last so long.
If you do prefer the polished look, use as mild a method as possible to clean the copper. I would suggest electrolysis or some brasso (or any cleaner used to clean copper cookware and fixtures) and a soft cloth.
Oh, BTW, the clear coat idea will not work! I've tried it. You do end up with a most interesting glossy-looking dark jade green patina though! most clear coat is still porus, and it lets some trace moisture and air through. This is why the above described look comes on. Now if you primed, painted the tubing copper, and cleared it, then it will stay shiny. You could try a laquer-based clearcoat, it may work, trouble is, most clearcoat is made to be used with a base coat. Some clearcoats are designed to be used on bare metal however. Try an auto parts store, and buy clear engine paint if you want to go this route. No guarantees, though, because I never tried it on copper personally, but it's your best bet if you want to clearcoat it.
To keep the oxidization away, polish your copper, and apply Renaissance Wax (Museum Replicas sells it) it used to keep replica swords and armor from oxidizing when in storage. it should work on copper too, and would mean more time between polishings.
The more you polish any metal, the more it wears away at the material, especially with softer metals. Not a problem if you will only use a launcher for a few years, but if you want to use it in say, 30 years from now, it may weaken the tubing a bit. you would be best off letting the copper develop a natural patina (the brown patina looks great on copper, imo)
some people go through all kinds of trickery to force copper to look weathered. The oxidization is what makes copper roofing and the Statue of Liberty last so long.
If you do prefer the polished look, use as mild a method as possible to clean the copper. I would suggest electrolysis or some brasso (or any cleaner used to clean copper cookware and fixtures) and a soft cloth.
Oh, BTW, the clear coat idea will not work! I've tried it. You do end up with a most interesting glossy-looking dark jade green patina though! most clear coat is still porus, and it lets some trace moisture and air through. This is why the above described look comes on. Now if you primed, painted the tubing copper, and cleared it, then it will stay shiny. You could try a laquer-based clearcoat, it may work, trouble is, most clearcoat is made to be used with a base coat. Some clearcoats are designed to be used on bare metal however. Try an auto parts store, and buy clear engine paint if you want to go this route. No guarantees, though, because I never tried it on copper personally, but it's your best bet if you want to clearcoat it.
To keep the oxidization away, polish your copper, and apply Renaissance Wax (Museum Replicas sells it) it used to keep replica swords and armor from oxidizing when in storage. it should work on copper too, and would mean more time between polishings.