FAIL!!!

[Heimo]

well I cannot let JSR have all the fail fame so, here is what happened

Today I decided that the time has come that I am going to make myself A hybrid. the hybrid I am going to make is going to be made from T6 aluminum (6061) and every thing went smoothly except I forgot one small thing and that ruined the combustion chamber.

I started out as usual, to make a mold for the item I want to reproduce in metal (sorry for the crap picture my shop ain't well lit)


the mistake that ruined the chamber is visible in that picture I forgot to remove the paint from the metal pipe used as a core this created mold gas and this gas caused the failure.

here you can see a picture of the finished casting in its rough stage



every thing was still fine then, until I started to cut off the sprue's then I discovered a flaw in the casting



yep that is a bubble, it was caused by the burning paint on the steel pipe. this ruined the casting (the finished product will look much better than this, this is just before any finishing took place)

anyway I will try again next weekend

when I get a casting that I am satisfied with I will start a thread in the discussion aria

just out of curiosity this chamber has id of 35mm and a wall thickness of 10mm anybody care to calculate the burst pressure?

[SpudBlaster15]

Lorem ipsum dolor sit amet, consectetur adipiscing elit. Cras nec placerat erat. Vivamus dapibus egestas nunc, at eleifend neque. Suspendisse potenti. Sed dictum lacus eu nisl pretium vehicula. Ut faucibus hendrerit nisi. Integer ultricies orci eu ultrices malesuada. Fusce id mauris risus. Suspendisse finibus ligula et nisl rutrum efficitur. Vestibulum posuere erat pellentesque ornare venenatis. Integer commodo fermentum tortor in pharetra. Proin scelerisque consectetur posuere. Vestibulum molestie augue ac nibh feugiat scelerisque. Sed aliquet a nunc in mattis.

[POLAND_SPUD]

you're joking right?? that looks great even if it failed

[Heimo]

you'll need to artificially age harden the chamber post casting.

it was my original intentions to do so.

one more thing I forgot to do, is to degas the melt. if I degas the melt and I pour through a filter to remove the impurities I guess I could get pretty decent results the failed casting is going to get recycled but first I am going to cut it up to have a look on the inside

something else I may do is to cast this in aluminum bronze, this is a high strength alloy used to make non sparking tools anybody else think this is a good idea? or should I cast this in normal brass the same type used to make plumbing fittings if you guys think that aluminum bronze is overkill.

I only used a steel pipe to create a core because I was too lazy to make a core box

something else I would really like to do is to cast this in gunmetal/red brass unfortunately I have been unable to find a source

So what do you guys think aluminum/plumbing brass/aluminum bronze/Japanese art bronze or gunmetal? (I will have to alloy the gunmetal myself though) any other suggestions?

thanks Poland_ spud but wait till you see the next one, cause this one is crap in my book the next next one will be of higher standard

[Mr.Sandman]

That look very good even as a failure, I love metal casting and am thinking of rebuilding my foundry as it has become dilapidated over the years. I think we should have a metal casting/machining section to this site.

[clemsonguy1125]

That look very good even as a failure, I love metal casting and am thinking of rebuilding my foundry as it has become dilapidated over the years. I think we should have a metal casting/machining section to this site.

That would be great, did your mini metal lathe work well

[Mr.Sandman]

That look very good even as a failure, I love metal casting and am thinking of rebuilding my foundry as it has become dilapidated over the years. I think we should have a metal casting/machining section to this site.

That would be great, did your mini metal lathe work well

Not trying to thread hijack but I never received the lathe, it's on backorder for quite a bit, I shall see how long I can hold out. On that note harbor freight has a new website design clicky.